Polyethylene Film Grade LL 0209AA (Stabilization), Thickness: 38 microns, Blow up Ratio (150*2.3 mm die): 2:1, Max Output Rate: 50 kg/hr, Melt Flow rate (2.16 kg): 0.9 g/10 min, Test Method: ISO 1133, Density: 920 kg/m3, Test Method: ISO 1872/1, Vicat Softening Temp.: 100 C, Test Method: ISO R 306-74, Tensile Strength at yield MD/TD: 10/11 MPa, Test Method: ISO R 1184, Tensile Strength at break MD/TD: 41/32 MPa, Test Method: ISO R 1184, Elongation at break MD/TD: 620/840 %, Test Method: ISO R 1184, Tear Strength MD/TD: 145/370 g/25 mic, Test Method: ASTMD 1922-67, Dart Impact Stength: 150 g, Test Method: ASTMD 1709-75.